Polynil® P240 LHSV

Chemical Family: Polyamides

Nilit POLYNIL® P240 LHSV is a high viscosity unreiforced Polyamide 66 (Nylon 66) for injection molding.This high molecular weight 5 viscosity Polyamide 66 resin is heat stabilized and designed for improved wear resistance and melt strenght.

Product families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: Polynil
Polymer Name: Polyamide 66 (PA 66)
Flexural Modulus: 2700.0 - 2700.0 MPa
Additives Included: Heat Stabilizer
Processing Methods: Injection Molding
Technology: Plastics
Material Features: Heat Stabilized
Wear Resistant
Country Availability: Brazil
Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 4

9 rows

Characteristic	Value	Unit	Method
Tensile Modulus	2700	MPa	ISO 527
Yield stress	84	MPa	ISO 527
Flexural modulus, 23°	2700	MPa	ISO 178
Charpy notched impact strength (+23°)	5	kJ/m2	ISO 179/1eA
Charpy impact strength (+23°)	N	kJ/m2	ISO 179/1eU
Charpy notched impact strength (-30°)	4	kJ/m2	ISO 179/1eA
Charpy impact strength (-30°)	N	kJ/m2	ISO 179/1eU
Strain at Break	min. 50	%	ISO 527
Izod notched impact strength, +23°	7	kJ/m2	ISO 180/1A

Table 2 of 4

3 rows

Characteristic	Value	Unit	Method
Molding shrinkage - normal	1.4	%	ISO 294-4, 2577
Molding shrinkage - parallel	1.4	%	ISO 294-4, 2577
Density	1140	kg/m3	ASTM D 792

Table 3 of 4

5 rows

Characteristic	Value	Unit	Method
Temperature of deflection under load (1.80 Mpa)	72	°C	ISO 75-1/-2
Temperature of deflection under load (0.45 Mpa)	225	°C	ISO 75-1/-2
Melting temperature (10°C/min)	258	°C	ISO 11357-1/-3
Oxygen index	28	%	ISO 4589-1/-2
Vicat softening temperature	240	°C	ISO 306

Table 4 of 4

1 row

Characteristic	Value	Unit	Method
Water absorption	8.5	%	Sim. to ISO 62