LOXIAMID PA6 HS1 IM3 03039
- Chemical Family
- Polyamides
LOXIAMID PA6 HS1 IM3 03039 is an injection molding grade of Polyamide 6 resin with excellent impact resistance.
Product families
Applications
- Consumer Goods — Furniture; Building & Construction — Other Building & Construction Applications
- Exterior & Body
- Interior
- Other Bonding & Assembly Applications
- Other Building & Construction Applications
Product Families
- Polyamides
Other characteristics
- Brand
- LOXIAMID
- Polymer Name
- Polyamide 6 (PA 6)
- Flexural Modulus
- 1900.0 - 1900.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Adhesives & Sealants
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Features
- Outstanding Impact Resistance
- Good Melt Fluidity
- High Dimensional Stability
- Good Impact Strength
- Excellent Heat, Chemical and Abrasion resistance
- High Stiffness and Rigidity
- Technology
- Plastics
- Product Safety
As long as the processing of our product is carried out in compliance with the processing instructions specified in the product data sheet, molten masses are thermally stable and are not a source of any danger due to molecular decomposition or the formation of gasses or vapor. According to the safety data sheet the user/processor is to ensure compliance with the specified occupational exposure limits through sufficient exhaust and ventilation in order to avoid any negative impact on the health and well-being of his/her employees. If processing is carried out at temperatures significantly below the specified processing temperatures then gaseous products of decomposition can form as a result of the partial decomposition of the polymer.
- Material Features
- Chemical Resistant
- Dimensional Stability
- Excellent Melt Flow
- Good Abrasion Resistance
- Good Impact Strength
- High Rigidity
- High Stiffness
- Very Good Heat Resistance
- Product Properties
The indicated test values represent approximate values but are not binding maximum or minimum values. It is possible that the values may be influenced or may deviate due to tool design, processing conditions, etc. The test values do not represent any contractual assurances regarding the properties or the suitability of the product for a specific intended application. All of the information, approximate values, descriptions, drawings, etc. included in the product data sheet can change at any time and do not represent any contractually agreed properties of our product.
- Plastics and Elastomers End Uses
- Fasteners
- Furniture
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
Table 2 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break | min. 50 | % | ISO 527 |
| Flexural Modulus | 1900 | MPa | ISO 178 |
| Flexural Strength | 60 | MPa | ISO 178 |
Table 3 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield | 40 | MPa | ISO 527 |
| Max. Moisture Content | 0.15 | % | — |
| Drying Temperature | 80 | °C | — |
| Drying Time | 2 - 4 | hrs | — |
| Melt Temperature | 240 - 285 | °C | — |
| Mold Temperatures | 65 - 80 | °C | — |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa) | 110 | °C | ISO 75 |
| Heat Deflection Temperature (1.8 MPa) | 53 | °C | ISO 75 |
Table 5 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Notched Impact | 80 | kJ/m² | ISO 180 |