LINCORE® PLA FF P2 40 400
- Chemical Family
- PolyestersPolylactic Acid (PLA)
LINCORE® PLA FF P2 40 400 is a fabric made of LINCORE® roving (commingled flax and PLA filaments). Consolidation is done by heating above melting temperature of PLA matric (170°C-200°C) and applying a low pressure (1-30 bars), before a cooling step under pressure.The molding can be realized by diaphragm (1 to 8 bars)- Thermo compression (10 to 200 bars) - Sandwich thermo compression (1 to 5 bars).
Product families
Applications
Applications
- Consumer Goods — Sports & Recreation
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
Building & Construction — Building Envelope & Roofing
- Other Building Envelope & Roofing Applications
Building & Construction — Building Materials
- Interior Fixtures
- Other Building Materials
- Structural Components
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Electrical & Electronics — Parts & Components
- Other Parts & Components
Industrial — Power, Water & Utilities
- Renewable Energy
Automotive & Transportation — Transportation
- Marine
- Rail & Mass Transit
Product Families
Plastics — Engineering & Specialty Polymers
- Biodegradable Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- LINCORE
- Polymer Name
- Polylactic Acid (PLA)
- Labeling Claims
- Biodegradable, Recyclable, VOC-free
- Biodegradable
- Recyclable
- VOC-free
- Fillers Included
- Flax Fibers
- Processing Methods
- Compression Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Benefits
- No voc emission
- Ease of storage conditions
- Recyclability
- Drapability
- Features
- Fast Processing Cycle Time
- Weight Saving
- Low Pressure Molding
- 100% Green Material
- Technology
- Plastics
- Material Features
- Fast Cycle Times
- Light Weight
- Recyclable
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Construction Applications
- Energy Storage
- Industrial Parts
- Marine Applications
- Sporting Goods
- Plastics and Elastomers Processing Methods
- Compression Molding
Technical data
Table 1 of 1
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 99.5 +/- 8.2 | MPa | ISO 527 |
| Tensile Modulus | 13.7 +/- 0.4 | GPa | ISO 527 |
| Tensile Elongation | 1.4 +/-0.1 | % | ISO 527 |
| Flexural Strength | 125.8 +/- 6.1 | MPa | ISO 14125 |
| Flexural Modulus | 12.6 +/- 0.9 | GPa | ISO 14125 |
| Flax Content | 40 | % | — |