Grupo Repol B1S25 G25
- Chemical Family
- Polyamides
Grupo Repol B1S25 G25 is 25% Glass Fiber Reinforced Nylon 6.
Product families
Applications
Applications
- Consumer Goods — Furniture; Agriculture & Feed — Other Agriculture & Feed Applications; Automotive & Transportation — Other Automotive & Transportation Applications; Building & Construction — Other Building & Construction Applications; Electrical & Electronics — Other Electrical & Electronics Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
HI&I Care — Institutional & Industrial Care
- Vehicle & Machinery
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 7000.0 - 7000.0 MPa
- Markets
- Agriculture & Feed
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- HI&I Care
- Technology
- Plastics
- Material Features
- Low Moisture Absorption
- Plastics and Elastomers End Uses
- Furniture
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.31 | g/cc | ISO 1183/A |
| Moisture Absorption at Equilibrium | max. 0.25 | % | Karl-Fischer; ISO 15512/A |
| Tensile Strength at Break | 155 | MPa | ISO 527 |
| Elongation at Break | 3.5 | % | ISO 527 |
| Flexural Strength | 220 | MPa | ISO 178 |
| Flexural Modulus | 7 | GPa | ISO 178 |
| Izod Impact, Notched (ISO) at Temperature 23.0°C | 10 | kJ/m2 | ISO 180/1A |
| Charpy Impact Unnotched at Temperature 230°C | 7.5 | J/cm2 | ISO 179/1e1J |
| Charpy Impact, Notched at Temperature 23.0°C | 1.1 | J/cm2 | ISO 179/1eA |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 | °C | ISO 75/A |
| Vicat Softening Point | min. 200 | °C | 50 N; ISO 306 |