Synofin (Modified PPCP) LA4713/LA4613 IM Talc Filled 20

Chemical Family: PolyolefinsPolypropylenes (PP)

Gujarat Petrosynthese is modifying and supplying of PP Polymers with a high grade of raw material using the latest technology as per customer specification. These Synofin (Modified PPCP) LA4713/LA4613 IM Talc Filled 20 polymers are modified with Flame Retardant, UV, Glass Fiber, Talc, etc.

Product families

Applications

Consumer Goods — Appliances & Electronics; Consumer Goods — Cold-Chain & Insulation; Consumer Goods — Other Consumer Goods Applications

Automotive & Transportation — Automotive

Safety Systems
Seating

Electrical & Electronics — Parts & Components

Connectors

Electrical & Electronics — Wire & Cable

Optical Fiber & Telecom

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Other characteristics

Brand: Synofin (Modified PPCP)
Polymer Name: Polypropylene Copolymer
Melt Flow Index: 6.0 - 10.0 g/10 min
Fillers Included: Talc
Processing Methods: Injection Molding
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Technology: Plastics
Plastics and Elastomers End Uses: Appliances
Child Safety Seats
Connectors
Garden Equipment
Lawn Equipment
Seat Belts
Seat Webbing
Telecommunications
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 3

5 rows

Characteristic	Value	Unit	Method
Tensile Strength at Yield 50 mm/min	18 - 22	MPa	D 638
Tensile Elongation at Yield	12-16	%	D638
Flexural Strength 5 mm/min	22 - 26	MPa	D790
Flexural Modulus	1300- 1400	MPa	D790
Izod Notched Impact Strength	90-120	J/m	D256

Table 2 of 3

3 rows

Characteristic	Value	Unit	Method
Melt Flow Index at 230C & 2.16 Kg load	6-10	gms/ 10 min	D 1238
Density	1.00 – 1.08	g/cc	D 792
Filler Content	19 – 21	%	D 5630

Table 3 of 3

2 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature Under Load (B)1.82MPa	65 - 72	C	D 648
Vicat Softening Temperature (B)	140 - 145	C	D 1525