FluoroGrip® F (HD-FEP) Teflon®
- Chemical Family
- FluoropolymersPolyolefins
FluoroGrip® F (HD-FEP) Teflon® is made from high molecular weight resin for applications where chemical resistance, high flex life and stress-crack-resistant performance are required.
Properties
- Physical Form
- Film
Other characteristics
- Brand
- FluoroGrip
- Density
- 2120.0 - 2170.0 kg/m³
- Features
Chemical Resistant, Crack Resistant, Flexible, Good Optical Properties, Good Thermal Stability, Good Weather Stability, High Molecular Weight, High Performance, Non Stick, Very Low Surface Energy
- Polymer Name
- Perfluoroethylene Propylene Copolymer (FEP)
- Tensile Modulus
- 480.0 - 480.0 MPa
- Markets
- Adhesives & Sealants
- Building & Construction
- Food & Nutrition
- Printing & Packaging
- Availability
FluoroGrip® – F is available standard with an advanced pressure sensitive adhesive (PSA) of acrylic or high temperature resistant silicone PSA. Special chemical resistant adhesives are available.. Available Thicknesses (Film Only; Not Including Adhesive) - 2 mil, 5 mil, 10 mil, 20 mil, 30mil.
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Certifications
FluoroGrip® – F is designed to meet the requirements to comply with the FDA's Register of Food Additive Regulations.
- Labeling Claims
- Food Contact Acceptable
- Product Families
- Plastics — Parts, Shapes & Films
- Material Features
- Chemical Resistant
- Crack Resistant
- Flexible
- Good Optical Properties
- Good Thermal Stability
- Good Weather Stability
- High Molecular Weight
- High Performance
- Certifications and Compliance
- FDA Compliant
- UL 94
- Plastics and Elastomers End Uses
- Film
- Pipe Wraps
- Release Film
- Tank Liner
- Tape
Technical data
Table 1 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Break | 24.0 | MPa | ASTM D-882 |
| Elongation at Break | 300.0 | % | ASTM D-882 |
| Tensile Modulus | 480.0 | MPa | ASTM D-882 |
| Initial Tear Strength (1 mil) | 2.2 - 2.7 | N | ASTM D-1004 |
| Initial Tear Strength (2 mil) | 4.9 - 5.3 | N | ASTM D-1004 |
| Propagating Tear Strength (1 mil) | 1.4 - 1.5 | N | ASTM D-1922 |
| Propagating Tear Strength (1 mil) | 2.4 - 2.7 | N | ASTM D-1922 |
| Fold Endurance (M.I.T.) | 10000.0 | cycles | ASTM D-2176 |
Table 2 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Oxygen Index | 95.0 | % | ASTM D-2863-77 |
| Specific Gravity | 2.12 - 2.17 | — | ASTM D-792 |
| Melt Point (DTA) | 500.0 | °F | ASTM D-3418 |
| Yield (1mil film) | 18.0 | m²/kg | — |
| Flammability | V - 0 | — | ASTM UL-94 |
| Water Absorption (24 hrs) | max. 0.01 | % | — |
| Hardness | D55 | Shore D | ASTM D-785 |
| Elongation at Break (RT) | 300.0 | % | ASTM D-882 |
| Tensile Strength at Break | 3000.0 | psi | ASTM D-882 |
| Low Temperature Embrittlement | VTM-0 | °F | — |
Table 3 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Point | 252 - 282 | °C | ASTM D-3418 |
| Continuous Service Temp (Acrylic Adhesive) | 163.0 | °C | — |
| Continuous Service Temp (Silicone Adhesive) | 206.0 | J/(k°K) | — |
| Specific Heat | 1172.0 | w/(m°K) | — |
| Coefficient of Thermal Condctvty | 0.195 | mm | — |
| Coefficient of Linear Thermal Expansion | 9.9 x 10⁻⁵ | (mm°C) | ASTM D-696 |
| Limiting Oxygen Index | 95.0 | % | ASTM D-2863 |
Table 4 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Strength (1 mil) | 240.0 | kV/mm | ASTM D-149 |
| Dielectric Constant (1kHz) | 2.1 | — | ASTM D-150 |
| Dissipation Factor (1kHz) | 0.0003 | — | ASTM D-150 |
Table 5 of 6
2 rows| Characteristic | Value |
|---|---|
| 2000 Hours Salt Fog | Pass |
| 500 hours SO₂ | Pass |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Refractive Index | 1.341 - 1.347 | — | ASTM D-542 |
| Solar Transmission | 96.0 | % | ASTM E-424 |