RIABLEND® A 029 XE4291 schwarz
RIABLEND® A 029 XE4291 schwarz is in Black. RIABLEND® ® product line includes all plastic compounds that consist of at least two polymers. On the one hand, we combine polymers that can be easily combined with one another due to their chemical structure. On the other hand, our blends are also polymers that would not necessarily go together straight away, which we combine using a compatibilizer. With our egg-laying wool milk sow, you have a multitude of possible combinations - and thus also various properties of the plastics - at your disposal.
Product families
Applications
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- RIABLEND
- Polymer Name
- PC/ABS Alloy
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Automotive & Transportation
- Features
- Amorphous
- Processing
- Injection Molding
- Technology
- Plastics
- Fillers Included
- Glass Fiber
- Material Features
- Amorphous
- Chemical Resistant
- Good Damping
- Good Mechanical Properties
- High Gloss
- Low Moisture Absorption
- Low Water Absorption
- Tribological Modified
- Regional Availability
- Europe
- Plastics and Elastomers End Uses
- Automotive Exterior Trim
- Automotive Interior Trim
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt volume-flow rate, MVR | 18 | cm³/10min | ISO 1133 |
| Temperature | 260 | °C | — |
| Load | 5 | kg | — |
| Molding Shrinkage, normal | 0.3 | % | ISO 294-4, 2577 |
Table 2 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 6800 | MPa | ISO 527 |
| Yield Stress | 110 | MPa | ISO 527 |
| Yield Strain | 3.7 | % | ISO 527 |
| Stress at break | 107 | MPa | ISO 527 |
| Strain at Break | 3.8 | % | ISO 527 |
| Charpy Impact Strength (+23°C) | 65 | kJ/m² | ISO 179/1eU |
| Charpy Impact Strength (-30°C) | 70 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength (+23°C) | 14.6 | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength (-30°C) | 11.5 | kJ/m² | ISO 179/1eA |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Temp. of deflection under load, 1.80 MPa | 133 | °C | ISO 75-1/-2 |
| Temp. of deflection under load, 0.45 MPa | 137 | °C | ISO 75-1/-2 |
| Vicat softening temperature, B | 139 | °C | ISO 306 |
| Burning behav. at thickness h | HB | class | IEC 60695-11-10 |
| Thickness Tested | 1 | mm | — |
Table 4 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | min. 1E13 | Ohm*m | IEC 62631-3-1 |
| Surface Resistivity | 10000000000000 | Ohm | IEC 62631-3-2 |
| Comparative tracking index | 175 | — | IEC 60112 |
Table 5 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | min. 1E13 | Ohm*m | IEC 62631-3-1 |
| Surface Resistivity | 10000000000000 | Ohm | IEC 62631-3-2 |
| Comparative tracking index | 175 | — | IEC 60112 |