To catalogue
SITRADUR® TF20 / C94150
- Chemical Family
- Polyesters
Sitradur® TF20 / C94150 is a polybutylene terephthalate (PBT) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding.
Product families
Applications
Applications
- Electrical & Electronics — Other Electrical & Electronics Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- SITRADUR
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- Glass Fiber
- Additives Included
- Flame Retardant, Lubricant (PTFE)
- Flame Retardant
- Lubricant (PTFE)
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Industrial
- Material
Polybutylene terephthalate with 20% PTFE content, Injection molding
- PACKAGING
Standard packaging includes the 25-kg-bag and the 1000 kg octabin (octagonal container). Other forms of packaging are possible subject to agreement.
- Technology
- Plastics
- Packaging Type
- Bags
- Application Areas
Molded parts with wear-resistant properties and reduced sliding friction values.
- Material Features
- Excellent Transparency Properties
- Good Flow
- Laser Weldable
- Low Friction
- Lubricated
- Wear Resistant
- HIGHLIGHTS
- Good flowability
- Part Identification
- >PBT+PTFE<
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Module (1 mm/min) | min. 2300 | MPa | ISO 527 - 1, - 2 |
| Breaking Stress (5 mm/min) | min. 40 | MPa | ISO 527 - 1, - 2 |
| Elongation At Break (5 mm/min) | min. 4 | % | ISO 527 - 1, - 2 |
| Charpy Impact Strength (23°C) | min. 20 | kJ/m² | ISO 179 - 1eU |
| Charpy Impact Strength (23°C) | min. 1,5 | kJ/m² | ISO 179 - 1eA |
Table 2 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (50°C/h; 50N) | 170.0 | °C | ISO 306 |
| Burning Behavior (1,5 mm) | HB | Klasse | In Anl. UL94 |
Table 3 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Filler content (PTFE) | 20.0 | % | — |