Atomet 1001
- Chemical Family
- Iron & Iron Compounds
Rio Tinto Metal Powders Atomet 1001 is a highly compressible, water-atomized steel powder specifically designed for high density, high strength powder metallurgy and powder forging applications.
Properties
- Physical Form
- Powder
Product families
Applications
- Metal Manufacturing & Finishing
Product Families
- Alloys
Other characteristics
- Brand
- Atomet
- Markets
- Industrial
- Density
- Density measured in water.
- Features
High compressibility - due to its superior compressibility, Atomet 1001 can be single pressed to 7.2g/cm3 or repressed to densities up to 7.4 g/cm3.; Extends the performance levels of P/M parts.; Provides enhanced compaction capability.; Provides higher strength, higher density P/M parts.; Hardenability - the manganese level of Atomet 1001 is precisely controlled to provide optimal heat-treated properties without sacrificing compressibility.; Improved hardness and tensile properties.; Dimensional change - Atomet 1001 can be used with existing tooling designed for conventional water-atomized powders.; No need to retool; Consistency - a stable ore base and ultra-modern processing capability, including SPC, assure lot-to-lot consistency.; Improved P/M part consistency; Purity and cleanliness - state-of-the-art clean steel practices and a proprietary powder manufacturing process produce a powder with exceptionally low levels of residuals and inclusions.; Improved mechanical and dynamic properties of powder forged parts.; Improved machinability of P/M and P/F parts.
- Technology
- Base Chemicals & Intermediates
- Particle Size Analysis
- U.S. mesh µm
- Chemical Base
- Good Mechanical Properties
- Improved Strength
Technical data
Table 1 of 1
8 rows| Characteristic | Value | Unit |
|---|---|---|
| Carbon | 0.004 | wt% |
| Oxygen | 0.09 | wt% |
| Sulfur | 0.01 | wt% |
| Manganese | 0.18 | wt% |
| Iron | min. 99.4 | wt% |
| Apparent Density | 2.95 | g/cm³ |
| Flow | 26.0 | s/50g |
| Density* (600MPa) | 7.1 | g/cm³ |