G-PAEK™ 1100ESG

Chemical Family: Polyether Ketone (PEK)

G-PAEK™ 1100ESG is Ultra high Performance thermoplastic polymer, virgin, semicrystalline granules suitable for stock shapes extrusion, easy flow, Beige in color.

Properties

Physical Form: Granules
Solid

Product families

Applications

Automotive & Transportation — Other Automotive & Transportation Applications; Building & Construction — Other Building & Construction Applications; Industrial — Other Industrial Applications

Automotive & Transportation — Automotive

Other Automotive Applications

Building & Construction — Building Materials

Other Building Materials

Industrial — Chemical & Industrial Manufacturing

Other Industrial Applications

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: G-PAEK
Polymer Name: Polyether Ketone (PEK)
Flexural Modulus: 4100.0 - 4100.0 MPa
Processing Methods: Extrusion
Color: Beige
Markets: Automotive & Transportation
Building & Construction
Industrial
Flame Rating: UL 94 V0
Technology: Plastics
Material Features: Abrasion Resistant
Chemical Resistant
High Glass Transition Temperature
High Heat Deflection Temperature
High Temperature Resistance
High Temperature Strength
Low Water Absorption
Semi Crystalline
Recommended Applications: Suitable for high temperature applications, high wear & abrasion resistance, and high chemical resistance is required & for metal replacement with plastics etc.
Certifications and Compliance: UL 94
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Extrusion

Technical data

Table 1 of 6

7 rows

Characteristic	Value	Unit	Method
Flexural Strength	185	MPa	ASTM D 790
Compressive Strength	135	MPa	ASTM D 695
Elongation at Break	20-25	%	ASTM D 638
Flexural Modulus	4.1	GPa	ASTM D 790
Izod Impact Strength(Notched)	60	J/m	ASTM D 256
Tensile Modulus	4.2	GPa	ASTM D 638
Tensile Strength	110	MPa	ASTM D 638

Table 2 of 6

4 rows

Characteristic	Value	Unit	Method
Continuous Use Temperature ( Expected)	280	°C	UL 746B
Glass Transition Temperature (Tg)	152	°C	ASTM D 3418
Heat Deflection Temperature (HDT)	175	°C	ASTM D 648
Melting Point (Tm)	372	°C	ASTM D 3418

Table 3 of 6

6 rows

Characteristic	Value	Unit	Method
Density at 23°C	1.3	g/cc	—
Mold Shrinkage (400°C nozzle, 210°C Mold) ( Across Flow)	1.3	%	—
Mold Shrinkage (400°C nozzle, 210°C Mold) ( Along Flow)	1	%	—
Water Absorption	0.04	%	ASTM D 570-98
Hardness	86	Shore D	D 2240-05
Rockwell Hardness	100	Scale R	785/M Scale

Table 4 of 6

1 row

Characteristic	Value	Method
Flammability	V-0	UL 94/0.8 mm

Table 5 of 6

5 rows

Characteristic	Value	Unit
Drying Temperature at 150°C	4-6	hr
Hopper/ Throat Temperature	60-80	°C
Mold Temperature	200-220	°C
Nozzle Temperature	400	°C
Temperature Settings	390-400	°C

Table 6 of 6