DISTITRON® 1402 AST
DISTITRON® 1402 AST - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce pipes and tanks through hand lay up and spray up method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- End Uses
- Pipes, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
- Hand Lay-up, Spray Lay-up
- Color
- Pink
- Markets
- Building & Construction
- Industrial
- Shelf LIfe
- 3 Months (23°C in Dark )
- Technology
- Composite Materials
- Product Safety
Stir the resin before use, without use air bubbles, As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.
- Application Methods
- Spray
- Composites End Use
- Pipes
- Tanks
- Material Features
- Good UV Protection
- HIGHLIGHTS
- Paraffinated
- Preaccelerated
- Light stabilized
- Thixotropic
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Hand Lay-up
- Spray Lay-up
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific weight at 20°C | 1, 11 | g/cm3 | — |
| Solid Content | 58 - 62 | % | MT-CU001C |
| Exothermic peak at 20°C + 1,5% MEKP50 | 170 - 200 | °C | RS.08.G |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 470 - 650 | mPa.s | MT-CUT25V |
| Gel Time at 20°C + 1,5% MEKP50 | 15 - 20 | minutes | RS.08.G |
| Delta at 20°C + 1,5% MEKP50 | 8 - 14 | minutes | RS.08.G |
Table 2 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 1, 4 | % | ISO 527 (2012) |
| Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 50 | MPa | ISO 527 (2012) |
| HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 75 | °C | ISO 75 -2A (2013) |
| Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 105 | MPa | ISO 178/B (2010) |
| Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 4000 | MPa | ISO 527 (2012) |
| Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3800 | MPa | ISO 178/B (2010) |
| Glass transition at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 90 | °C | ASTM E 1545 (2011) |
| Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 45 | — | ASTM D 2583 (2007) |