DISTITRON® VE 100 H
DISTITRON® VE 100 H - Bisphenol-A Epoxy Resin based vinyl ester in styrene. It is used to produce pipes and tanks,production of gelcoat,profiles,putties through filament winding,mix with fillers and/or additives,pultrusion method.
Identification
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Automotive & Transportation — Transportation
- Marine
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- End Uses
- Pipes, Tanks
- Polymer Name
- Vinyl Ester Resin
- Processing Methods
- Filament Winding, Pultrusion
- Color
- Yellow
- Markets
- Automotive & Transportation
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Composites End Use
- Pipes
- Tanks
- HIGHLIGHTS
- Clear unaccelerated
- High stability
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Filament Winding
- Pultrusion
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 54 - 58 | % | MT-CU001C |
| Specific weight at 20°C | 1,06 | g/cm3 | — |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 380 - 480 | mPa.s | MT-CU025V |
| Gel Time at 25°C + 0,5% Co 6% + 1,5% CuHP | 9-15 | minutes | RS.08.G |
| Delta at 25°C + 0,5% Co 6% + 1,5% CuHP | 9-15 | — | RS.08.G |
| Exothermic peak at 25°C + 0,5% Co 6% + 1,5% CuHP | 155 - 185 | °C | RS.08.G |
| Acidity at 25°C + 0,5% Co 6% + 1,5% CuHP | max. 8 | mg KOH/g | MT-CU001I |
Table 2 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 36 | — | ASTM D 2583 (2007) |
| Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3300 | MPa | ISO 178/B (2010) |
| Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 145 | MPa | ISO 178/B (2010) |
| Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3400 | MPa | ISO 527 (2012) |
| Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 85 | MPa | ISO 527 (2012) |
| HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 104 | °C | ISO 75 -2A (2013) |
| Glass transition at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 108 | °C | ASTM E 1545 (2011) |
| Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 6,6 | % | ISO 527 (2012) |