DISTITRON® 436 T100
DISTITRON® 436 T100 - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce buttons through casting (rods) method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- Polymer Name
- Polyester (unspecified)
- Color
- Blue
- Markets
- Building & Construction
- Shelf LIfe
- 3 Months (23°C in Dark )
- Technology
- Composite Materials
- Product Safety
Stir the resin before use, without use air bubbles
- HIGHLIGHTS
- With antifoaming additive
- Clear unaccelerated
- Thixotropic
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Brookfield Viscosity at 25°C, sp 3 rpm 20 | 2500 - 4200 | mPa.s | MT-CUT25V |
| Solid Content | 70 - 74 | % | MT-CU001C |
| Gel Time at 25°C + 0,6% Co 1% + 1%MEKP50 | 7-11 | minutes | RS.08.G |
| Delta at 25°C + 0,6% Co 1% + 1%MEKP50 | 16 - 23 | minutes | RS.08.G |
| Exothermic peak at 25°C + 0,6% Co 1% + 1%MEKP50 | 115 - 145 | °C | RS.08.G |
| Specific weight at 20°C | 1,12 | g/cm3 | — |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile strength at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 35 | MPa | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 1800 | MPa | ISO 527 (2012) |
| HDT at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 39 | °C | ISO 75 -2A (2013) |
| Glass transition at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 47 | °C | ASTM E 1545 (2011) |
| Barcol Hardness at 25°C at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 32 | — | ASTM D 2583 (2007) |
| Elongation at break at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 11,0 | % | ISO 527 (2012) |