DISTITRON® 1303
DISTITRON® 1303 - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce abrasives,chips,putties through casting,mix with fillers and/or additives method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- Polymer Name
- Polyester (unspecified)
- Color
- Yellow
- Markets
- Building & Construction
- Shelf LIfe
- 3 Months (23°C in Dark )
- Technology
- Composite Materials
- HIGHLIGHTS
- Clear unaccelerated
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific weight at 20°C | 1, 14 | g/cm3 | — |
| Delta at 20°C + 1,5% MEKP50 | 3:30 - 6:30 | minutes | RS.08.G |
| Solid Content | 69 - 73 | % | MT-CU001C |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 950 - 1150 | mPa.s | MT-CUT25V |
| Gel Time at 20°C + 1,5% MEKP50 | 4:30 - 7:30 | minutes | RS.08.G |
| Exothermic peak at 20°C + 1,5% MEKP50 | 140 - 170 | °C | RS.08.G |
| Acidity at 20°C + 1,5% MEKP50 | 10 - 16 | mg KOH/g | MT-CU001I |
Table 2 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 110 | MPa | ISO 178/B (2010) |
| Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 52 | MPa | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 2600 | MPa | ISO 527 (2012) |
| Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 2400 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 48 | °C | ISO 75 -2A (2013) |
| Glass transition at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 57 | °C | ASTM E 1545 (2011) |
| Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 32 | — | ASTM D 2583 (2007) |
| Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 6, 0 | % | ISO 527 (2012) |