EPOVIA OPTIMUM® KRF 4031 TA
EPOVIA OPTIMUM® KRF 4031 TA - Bisphenol-A Epoxy Resin based vinyl ester in styrene. It is used to produce marine,boats,pools,surficial protection (liner,top coat) through hand lay up and spray up method.
Identification
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Automotive & Transportation — Transportation
- Marine
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- EPOVIA OPTIMUM
- End Uses
- Pipes, Tanks
- Polymer Name
- Vinyl Ester Resin
- Processing Methods
- Hand Lay-up, Spray Lay-up
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Product Safety
Stir the resin before use, without use air bubbles
- Application Methods
- Spray
- Composites End Use
- Pipes
- Tanks
- HIGHLIGHTS
- Preaccelerated
- Thixotropic
- High hydrolisys resistance
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Hand Lay-up
- Spray Lay-up
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 60 - 64 | % | MT-CU001C |
| Specific weight at 20°C | 1.00 - 1.10 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 450 - 550 | mPa.s | MT-CUT25V |
| Gel Time | 27 - 33 | minutes | MT-CU202R |
| Exothermic peak | 125 - 145 | °C | MT-CU202R |
| Peak (23°C) | 40 - 50 | — | — |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Curing Cycle at 23°C (at 100°C) | 24 (2) | hr | — |
| Flexural strength | 65 | MPa | ISO 178 (2011) |
| Tensile strength | 40 | MPa | ISO 527 (2012) |
| Tensile Modulus | 3400 | MPa | ISO 527 (2012) |
| Elongation at break | 1.35 | % | ISO 527 (2012) |
| Flexural modulus | 3460 | MPa | ISO 178 (2011) |
| HDT | 93 | °C | ISO 75 -2A (2013) |