ENYDYNE® H 98466 TAE
ENYDYNE® H 98466 TAE - Unsaturated polyester resin in styrene,DCPD. It is used as general purpose in hand lay up and spray up method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- ENYDYNE
- End Uses
- Pipes, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
- Hand Lay-up, Spray Lay-up
- Markets
- Building & Construction
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Product Safety
Stir the resin before use, without use air bubbles, As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.
- Application Methods
- Spray
- Composites End Use
- Pipes
- Tanks
- HIGHLIGHTS
- Low styrene content
- Preaccelerated
- Thixotropic
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Hand Lay-up
- Spray Lay-up
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific weight at 20°C | 1,10 | g/cm3 | — |
| Solid Content | 62 - 66 | % | MT-CU001C |
| Brookfield Viscosity at 23°C, sp 3 rpm 50 | 700 - 900 | mPa.s | MT-CUT23V |
| Reactivity at 23°C | 2 | % | MEKP50 |
| Gel Time | 32 - 38 | minutes | MT-CU127R |
| Exothermic peak | 70 - 110 | °C | MT-CU127R |
| Peak (23°C) | 75 - 95 | — | — |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile strength | 50 | MPa | ISO 527 (2012) |
| Curing Cycle at 40°C + 2 h at 90°C (at 120°C for HDT) | 16 (2) | hr | — |
| Tensile Modulus | 3100 | MPa | ISO 527 (2012) |
| Flexural strength | 95 | MPa | ISO 178 (2011) |
| Flexural modulus | 2950 | MPa | ISO 178 (2011) |
| HDT | 75 | °C | ISO 75 -2A (2013) |
| Elongation at break | 2,8 | % | ISO 527 (2012) |