Polynt Group SMC VE 3700
Polynt Group SMC VE 3700 is a sheet molding compound based on a vinylester resin reinforced with glass fibers. This SMC has been developed for structural parts. SMC VE 3700 joint good mechanical properties, excellent heat resistance and high chemical resistance. SMC VE 3700 is formulated according to RoHS, REAC regulation SVHC and WEEE European legislation.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Product Families
Composite Materials — Prepregs & Molding Compounds
- Sheet Molding Compounds (SMC)
Other characteristics
- End Uses
- Pipes, Tanks
- Functions
- Molding Compound
- Markets
- Industrial
- Technology
- Composite Materials
- Composites End Use
- Pipes
- Tanks
- Material Features
- Chemical Resistant
- Flame Retardant
- Good Mechanical Properties
- Handling
Storage at 15-25°C, in dry ambient and out of direct sun light; Molding time 40 s/mm; Molding pressure 70 - 110 bar; Molding temperature 140 – 160°C
- Composite Materials Functions
- Molding Compound
Technical data
Table 1 of 1
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Rockwell Hardness | 70 | HRm | ISO 2039-2 |
| Flexural modulus | 10 | MPa | ISO 14125A |
| Linear Shrinkage | 0,0 | % | ISO 2577 |
| Quantity of glass | 25 | % | — |
| Impact strength (Charpy) | 60 | KJ/m2 | ISO 179 |
| Density | 1,7 | g/cm3 | ISO 1183 |
| Surface resistivity | 10^14 | Ω | IEC 93 |
| Water absorption | max. 0,2 | % | ISO 62 Met. 1 |
| Flexural strength | 160 | MPa | ISO 14125A |
| Heat distortion temperature HDT | min. 250 | °C | ISO 75 |