Polynt Group BMC 700-23 VE C
Polynt Group BMC 700-23 VE C is a bulk molding compound based on vinylester resin and reinforced with glass fibers. BMC 700-23 VE C joint good mechanical properties and high chemical resistance. This BMC has been developed for application where is requested anti-static protection. BMC 700-23 VE C is formulated according to RoHS, REAC regulation SVHC and WEEE European legislation.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Product Families
Composite Materials — Prepregs & Molding Compounds
- Bulk Molding Compounds (BMC)
Other characteristics
- End Uses
- Pipes, Tanks
- Functions
- Molding Compound
- Markets
- Industrial
- Technology
- Composite Materials
- Composites End Use
- Pipes
- Tanks
- Material Features
- Chemical Resistant
- Good Mechanical Properties
- Handling
Storage at 15-25°C, in dry ambient and out of direct sun light; Molding time 30 s/mm; Molding pressure 60 - 110 bar; Molding temperature 140 - 160°C
- Certifications and Compliance
- REACH (Europe)
- Composite Materials Functions
- Molding Compound
Technical data
Table 1 of 1
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Rockwell Hardness | 80 | Scale M | ISO 2039-2 |
| Glass fibre Content | 23 | % | — |
| Flexural strength | 100 | MPa | ISO 14125A |
| Flexural modulus | 10 | MPa | ISO 14125A |
| Impact strength (Charpy) | 35 | KJ/m2 | ISO 179 |
| Heat distortion temperature HDT | min. 200 | °C | ISO 75 |
| Linear Shrinkage | 0,0 | % | ISO 2577 |
| Density | 1,7 | g/cm3 | ISO 1183 |
| Water absorption | max. 0,2 | % | ISO 62 Met. 1 |
| Surface resistivity | max. 10^9 | — | — |