Polynt Group SMC LPMC 7000 LP
Polynt Group SMC LPMC 7000 LP is a sheet molding compound based on an unsaturated polyester resin reinforced with glass fibers. SMC LPMC 7000 LP is studied to be molded at low pressure. This SMC has been developed for structural parts SMC LPMC 7000 LP joint good mechanical properties and good varnish adhesion. SMC LPMC 7000 LP is formulated according to RoHS, REAC regulation SVHC and WEEE European legislation.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Product Families
Composite Materials — Prepregs & Molding Compounds
- Sheet Molding Compounds (SMC)
Other characteristics
- Functions
- Molding Compound
- Markets
- Building & Construction
- Technology
- Composite Materials
- Material Features
- Good Mechanical Properties
- Handling
Storage at 15-25°C, in dry ambient and out of direct sun light; Molding time 40 s/mm; Molding pressure 20 - 100 bar; Molding temperature 140 – 160°C
- Composite Materials Functions
- Molding Compound
Technical data
Table 1 of 1
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Rockwell Hardness | 80 | Scale M | ISO 2039-2 |
| Flexural modulus | 10 | MPa | ISO 14125A |
| Heat distortion temperature HDT | min. 200 | °C | ISO 75 |
| Linear Shrinkage | 0,0 | % | ISO 2577 |
| Density | 1,7 | g/cm3 | ISO 1183 |
| Impact strength (Charpy) | 70 | KJ/m2 | ISO 179 |
| Flexural strength | 160 | MPa | ISO 14125A |
| Quantity of glass | 27 | % | ISO 11667 |
| Length of glass | 25 | mm | — |
| Water absorption | max. 0,5 | % | ISO 62 Met. 1 |