NORSODYNE® S 81302 AL
NORSODYNE® S 81302 AL - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce transparent and corrugated sheets through continuous laminating,hand lay up and spray up method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- NORSODYNE
- End Uses
- Pipes, Structural Components, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
- Continuous Lamination, Hand Lay-up, Spray Lay-up
- Markets
- Building & Construction
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Application Methods
- Spray
- Composites End Use
- Pipes
- Structural Components
- Tanks
- Material Features
- Flame Retardant
- Good UV Protection
- HIGHLIGHTS
- Fire retardand properties
- Good transparence
- Light stabilized
- Medium reactivity
- Preaccelerated
- Very good glass wet-out
- Very long shelf life
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Continuous Lamination
- Hand Lay-up
- Spray Lay-up
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific weight at 20°C | 1,23 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 390 - 430 | mPa.s | MT-CU023V |
| Solid Content | 64 - 72 | % | MT-CU001C |
| Gel Time at 85°C + peroxydes | 2:00 - 2:40 | minutes | MT-CU026R |
| Curing Time at 85°C + peroxydes | 3:15 - 4:15 | minutes | MT-CU026R |
| Exothermic peak at 85°C + peroxydes | 208 - 223 | °C | MT-CU026R |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile strength at 80°C for 16hrs / at 120°C for +2hrs | 33 | MPa | ISO 527 (2012) |
| Tensile Modulus at 80°C for 16hrs / at 120°C for +2hrs | 4080 | MPa | ISO 527 (2012) |
| Elongation at break at 80°C for 16hrs / at 120°C for +2hrs | 1 | % | ISO 527 (2012) |
| Flexural strength for at 80°C for 16hrs / at 120°C for +2hrs | 50 | MPa | ISO 178 (2011) |
| Flexural modulus at 80°C for 16hrs / at 120°C for +2hrs | 4070 | MPa | ISO 178 (2011) |
| HDT at 80°C for 16hrs / at 120°C for +2hrs | 75,5 | °C | ISO 75 -2A (2013) |