DISTITRON® 161 T100Z

Chemical Family: Polyesters, Unsaturated Polyester (UPE)PolyestersUnsaturated Polyester (UPE)

DISTITRON® 161 T100Z - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce buttons through casting (rods) method.

Product families

Building & Construction — Building Envelope & Roofing

Building & Construction — Building Materials

Building & Construction — Infrastructure, Roads & Paving

Composite Materials — Polymers & Resins

Brand: DISTITRON
Polymer Name: Polyester (unspecified)
Markets: Building & Construction
Shelf LIfe: 3 Months (23°C in Dark )
Technology: Composite Materials
Product Safety: Stir the resin before use, without use air bubbles
HIGHLIGHTS: Thixotropic, With antifoaming additive
Handling: Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
Composite Materials Functions: Resins Binders & Matrix Materials

6 rows

Characteristic	Value	Unit	Method
Specific weight at 20°C	1, 1	g/cm3	—
Exothermic peak at 20°C + 1,5% MEKP50	135 - 165	°C	RS.08.G
Solid Content	67 - 71	%	MT-CU001C
Brookfield Viscosity at 25°C, sp 2 rpm 20	2900 - 3600	mPa.s	MT-CUT25V
Gel Time at 20°C + 1,5% MEKP50	19 - 24	minutes	RS.08.G
Delta at 20°C + 1,5% MEKP50	12-18	minutes	RS.08.G

5 rows

Characteristic	Value	Unit	Method
Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C	42	—	ASTM D 2583 (2007)
Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C	35	MPa	ISO 527 (2012)
Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C	2000	MPa	ISO 527 (2012)
HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C	42	°C	ISO 75 -2A (2013)
Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C	13,0	%	ISO 527 (2012)