DISTITRON® 417 DV20
DISTITRON® 417 DV20 - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce agglomerated and engineered stones through casting method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- Polymer Name
- Polyester (unspecified)
- Color
- Yellow
- Markets
- Building & Construction
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- HIGHLIGHTS
- Clear unaccelerated
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 69 - 73 | % | MT-CU001C |
| Brookfield Viscosity at 25°C, sp 3 rpm 20 | 1850 - 2150 | mPa.s | MT-CU025V |
| Gel Time at 25°C + 0,2% Co 6% + 2% AAP | 13 - 16 | minutes | RS.08.G |
| Delta at 25°C + 0,2% Co 6% + 2% AAP | 4:00 - 6:30 | minutes | RS.08.G |
| Exothermic peak at 25°C + 0,2% Co 6% + 2% AAP | 145 - 170 | °C | RS.08.G |
| Acidity at 25°C + 0,2% Co 6% + 2% AAP | 18 - 25 | mg KOH/g | MT-CU001I |
| Specific weight at 20°C | 1,15 | g/cm3 | — |
Table 2 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3400 | MPa | ISO 527 (2012) |
| Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 140 | MPa | ISO 178/B (2010) |
| Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 66 | MPa | ISO 527 (2012) |
| Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3200 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 46 | °C | ISO 75 -2A (2013) |
| Glass transition at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 56 | °C | ASTM E 1545 (2011) |
| Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 38 | — | ASTM D 2583 (2007) |
| Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 6,1 | % | ISO 527 (2012) |