Polynt Group HUP 27/25 RN-9010
Polynt Group HUP 27/25 RN-9010 is generally used in aeronautical, cosmetics applications.
Product families
Applications
Automotive & Transportation — Transportation
- Aerospace & Aviation
Product Families
Composite Materials — Prepregs & Molding Compounds
- Sheet Molding Compounds (SMC)
Other characteristics
- Functions
- Molding Compound
- Markets
- Automotive & Transportation
- Technology
- Composite Materials
- Handling
- Storage condition store dry at max
- 25 °C and out of direct sun light
- Molding time > 25 sec
- /mm
- Molding pressure > 100 bar
- Molding temperature > 145 °C
- Composite Materials Functions
- Molding Compound
Technical data
Table 1 of 1
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| fibre length | 25 | mm | DF PA3.01 |
| Curing Time | 90 | sec | ISO 12114/1 |
| surface weight | 3 | g/m2 | ISO 10352 |
| Flexural modulus | 9 | N/mm2 | ISO 14125 |
| fibre Content | 25 | % | ISO 1172 |
| Flexural strength | 150 | N/mm2 | ISO 14125 |
| impact strength | 60 | KJ/m2 | ISO 179 |
| Tensile strength | 60 | N/mm2 | ISO 527-4 |
| Specific Density | 193 | g/cm3 | ISO 1183 A |
| Shrinkage | 8 | % | ISO 2577 |
| heat distortion temperature | min. 200 | °C | IEC 60216 |
| Airbus qualification (QTR C-M-00358) | passed | — | AIMS05-35-002 |