Polynt Group BMC A 1000/22
Polynt Group BMC A 1000/22 is a bulk molding compound based on an unsaturated polyester resin, reinforced with glass fibers. This BMC has been developed for high chemical resistance applications as wash-machine or industrial equipment in contact with alkaline solution/detergent. Good mechanical properties and easy molding behavior are combined into the BMC a 1000/22. BMC a 1000/22 is formulated according to RoHS, REAC regulation SVHC and WEEE European legislation.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Product Families
Composite Materials — Prepregs & Molding Compounds
- Bulk Molding Compounds (BMC)
Other characteristics
- Functions
- Molding Compound
- Reinforcement Material
- Glass Fibers
- Markets
- Building & Construction
- Technology
- Composite Materials
- Material Features
- Chemical Resistant
- Handling
Storage in a dry place at 15-25°C, out of direct sunlight; Molding time 30 s/mm; Molding pressure 60 - 110 bar; Molding temperature 140 - 160°C
- Certifications and Compliance
- REACH (Europe)
- Composite Materials Functions
- Molding Compound
Technical data
Table 1 of 1
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Rockwell Hardness | 80 | Scale M | ISO 2039-2 |
| Heat distortion temperature HDT | min. 200 | °C | ISO 75 |
| Flexural strength | 90 | MPa | ISO 14125A |
| Flexural modulus | 9 | MPa | ISO 14125A |
| Quantity of glass | 22 | % | — |
| Impact strength (Charpy) | 30 | KJ/m2 | ISO 179 |
| Linear Shrinkage | 0,1 | % | ISO 2577 |
| Water absorption | 0,2 | % | ISO 62 Met. 1 |
| Density | 1,8 | g/cm3 | ISO 1183 |
| Surface resistivity | 10^14 | — | — |