NORSODYNE® Y 17185
NORSODYNE® Y 17185 - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce mastics,putties.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- NORSODYNE
- End Uses
- Pipes, Structural Components, Tanks
- Polymer Name
- Polyester (unspecified)
- Markets
- Building & Construction
- Industrial
- Shelf LIfe
- 9 Months (23°C in Dark )
- Technology
- Composite Materials
- Composites End Use
- Pipes
- Structural Components
- Tanks
- HIGHLIGHTS
- Very long shelf life
- High reactivity
- Preaccelerated
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
Technical data
Table 1 of 2
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 56 - 60 | % | MT-CU001C |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 170 - 230 | mPa.s | MT-CU023V |
| Gel Time at 23°C + 2% PBO50 | 1:30 - 2:30 | minutes | MT-CU162R |
| Peak at 23°C + 2% PBO50 | 4:30 - 7:30 | minutes | MT-CU162R |
| Exothermic peak at 23°C + 2% PBO50 | 100 - 120 | °C | MT-CU162R |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at break at 80°C for 16h / +2h at 120°C | 2,4 | % | ISO 527 (2012) |
| Curing Cycle at 80°C (120°C) | 16 (+2) | hr | — |
| Tensile strength at 80°C for 16h / +2h at 120°C | 65 | MPa | ISO 527 (2012) |
| Tensile Modulus at 80°C for 16h / +2h at 120°C | 3800 | MPa | ISO 527 (2012) |
| Flexural strength at 80°C for 16h / +2h at 120°C | 140 | MPa | ISO 178 (2011) |
| Flexural modulus at 80°C for 16h / +2h at 120°C | 4100 | MPa | ISO 178 (2011) |
| HDT at 80°C for 16h / +2h at 120°C | 90 | °C | ISO 75 -2A (2013) |