DISTITRON® 416 B1V12

Chemical Family: Polyesters, Unsaturated Polyester (UPE)PolyestersUnsaturated Polyester (UPE)

DISTITRON® 416 B1V12 - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce buttons through centrifugal casting method.

Product families

Building & Construction — Building Envelope & Roofing

Building & Construction — Building Materials

Building & Construction — Infrastructure, Roads & Paving

Composite Materials — Polymers & Resins

Brand: DISTITRON
Polymer Name: Polyester (unspecified)
Processing Methods: Centrifugal Casting
Color: Blue
Markets: Building & Construction
Shelf LIfe: 3 Months (23°C in Dark )
Technology: Composite Materials
HIGHLIGHTS: Clear unaccelerated
Handling: Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
Composite Materials Functions: Resins Binders & Matrix Materials
Composites Processing Methods: Centrifugal Casting

6 rows

Characteristic	Value	Unit	Method
Solid Content	69 - 73	%	MT-CU001C
Brookfield Viscosity at 25°C, sp 3 rpm 20	1050 - 1350	mPa.s	MT-CU025V
Gel Time at 25°C + 0,3% Co 1% + 1% MEKP50	5-8	minutes	RS.08.G
Delta at 25°C + 0,3% Co 1% + 1% MEKP50	12-17	minutes	RS.08.G
Exothermic peak at 25°C + 0,3% Co 1% + 1% MEKP50	135 - 165	°C	RS.08.G
Specific weight at 20°C	1,14	g/cm3	—

6 rows

Characteristic	Value	Unit	Method
Tensile strength at 70°C for 16h/ + 2h at 100°C /+ 1h at 100°C	65	MPa	ISO 527 (2012)
Tensile Modulus at 70°C for 16h/ + 2h at 100°C /+ 1h at 100°C	3200	MPa	ISO 527 (2012)
Flexural strength at 70°C for 16h/ + 2h at 100°C /+ 1h at 100°C	120	MPa	ISO 178/B (2010)
Flexural modulus at 70°C for 16h/ + 2h at 100°C /+ 1h at 100°C	2800	MPa	ISO 178/B (2010)
HDT at 70°C for 16h/ + 2h at 100°C /+ 1h at 100°C	50	°C	ISO 75 -2A (2013)
Elongation at break at 70°C for 16h/ + 2h at 100°C /+ 1h at 100°C	5,1	%	ISO 527 (2012)