DISTITRON® 411 V4
DISTITRON® 411 V4 - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce pipes and tanks through filament winding method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- End Uses
- Pipes, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
- Filament Winding
- Color
- Yellow
- Markets
- Building & Construction
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Composites End Use
- Pipes
- Tanks
- HIGHLIGHTS
- Clear unaccelerated
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Filament Winding
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 61 - 65 | % | MT-CU001C |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 300 - 400 | mPa.s | MT-CU025V |
| Reactivity 25°C - 35°C at 25°C + 1% Co 1% + 1,1% MEKP50 | 13 - 24 | minutes | RS.03.G |
| Peak at 25°C + 1% Co 1% + 1,1% MEKP50 | max. 40 | minutes | RS.03.G |
| Exothermic peak at 25°C + 1% Co 1% + 1,1% MEKP50 | 140 - 180 | °C | RS.03.G |
| Specific weight at 20°C | 1,11 | g/cm3 | — |
Table 2 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 135 | MPa | ISO 178/B (2010) |
| Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 44 | — | ASTM D 2583 (2007) |
| Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 80 | MPa | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3600 | MPa | ISO 527 (2012) |
| Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3500 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 78 | °C | ISO 75 -2A (2013) |
| Glass transition at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 94 | °C | ASTM E 1545 (2011) |
| Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3,5 | % | ISO 527 (2012) |