DISTITRON® 186
DISTITRON® 186 - Unsaturated polyester resin in styrene,Isophthalic. It is used to produce bmc and smc manufacture,very good mechanical properties through hot press molding method.
Product families
Applications
Automotive & Transportation — Transportation
- Marine
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- Polymer Name
- Polyester (unspecified)
- Processing Methods
- Compression Molding
- Color
- Yellow
- Markets
- Automotive & Transportation
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Material Features
- Good Mechanical Properties
- HIGHLIGHTS
- Clear unaccelerated
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Compression Molding
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 64 - 68 | % | MT-CU001C |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 2450 - 2850 | mPa.s | MT-CUT25V |
| Gel Time at 20°C + 1,5% MEKP50 | 160 - 200 | minutes | RS.08.G |
| Exothermic peak at 20°C + 1,5% MEKP50 | 10-17 | °C | RS.08.G |
| Acidity at 20°C + 1,5% MEKP50 | 10-17 | mg KOH/g | MT-CU001I |
| Specific weight at 20°C | 1,10 | g/cm3 | — |
Table 2 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 60 | MPa | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3900 | MPa | ISO 527 (2012) |
| Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3800 | MPa | ISO 178/B (2010) |
| Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 46 | — | ASTM D 2583 (2007) |
| Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 120 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 113 | °C | ISO 75 -2A (2013) |
| Glass transition at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 117 | °C | ASTM E 1545 (2011) |
| Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 1,8 | % | ISO 527 (2012) |