C-RAM FLX Neoprene FLX-1.0

Other characteristics

Brand

C-RAM FLX

Features

Abrasion Resistant, Flexible, Good Elongation, Good Weather Stability, High Tensile Strength, Tear Resistance, Thin Wall Thickness, Wide Temperature Operating Range

Polymer Name

Chloroprene Rubber (CR)

Markets

Automotive & Transportation

Typical Use

Neoprene elastomers are ideally suited for marine environments. They are easily painted and adhered. They are resistant to stack gas and salt water.

Availability

Standard product sizes for all grades are flat sheets 310 x 310 mm (12 x 12 in) and 400 x 500 mm (16 x 20 in) in the nominal thicknesses given in the above table. Specify the part as C-RAM FLX-xx, where xx is the nominal resonant frequency and include the dimensions.; Specify a urethane sheet as FLX-U, neoprene as FLX-N. FLX without a suffix designates silicone as a default.; We can supply other dimensions, and can diecut or water-jet parts to your drawings.; C-RAM FLX can also be supplied with a peeland-stick pressure sensitive adhesive backing. Specify by adding a /PSA suffix to the part name. It is also available with a metal foil reflective backing: specify by adding a /MTL suffix.

Show in full

Technology

Plastics

Disadvantages

Limited low temperature flexibility, fair resistance to aromatic and oxygenated solvents.

Product Families

Plastics — Parts, Shapes & Films

HIGHLIGHTS

C-RAM FLX is a series of flexible sheet materials which absorb approximately 99% of incident RF energy at design frequencies in the range of 1 to 35 GHz. The material is weatherproof and will withstand a wide temperature range. It will conform to complex shapes and is readily bonded to metal surfaces. C-RAM FLX is intended for attachment to aircraft structures, nose cones, ship masts, instrument housings, and other surfaces for the reduction of specular radar reflections

Show in full

Material Features

• Abrasion Resistant
• Flexible
• Good Elongation
• Good Weather Stability
• High Tensile Strength
• Tear Resistance
• Thin Wall Thickness
• Wide Temperature Operating Range

Application Methods

All C-RAM FLX rubber sheets must be in intimate contact with a metal surface for proper resonant behavior.; The normal method of applying C-RAM FLX silicone to a substrate is with a silicone RTV adhesive. For best results, the rubber sheet and the metal should be scuffed with sandpaper, wiped with alcohol to remove dust and grease, and have a silicone primer applied, such as CPRIME 215. The silicone adhesive, such as CBOND 255 or equivalent, is brushed or rolled onto one of the surfaces, and the sheet is then applied to the metal. Overnight cure is generally required, and a modest temperature cycle, such as a few hours at 150 ºF, helps the bond.; Alternately, a silicone caulking tube adhesive can also be used and does not require a primer. Simply apply a thin layer of adhesive, 2 to 4 mils thick, to the rubber sheet and the metal surface, and mate the two together, making sure to work the sheet down from one edge to the other to help prevent air entrapment.; For C-RAM FLX urethane, neoprene, and nitrile, scuff sand the back of the rubber sheet and the metal, and clean with alcohol of lacquer thinner. In certain applications it is good practice to prime the bare metal surface, and bond with a urethane adhesive, silicone adhesive, or neoprene contact adhesive. Temperature and application requirements dictate adhesive choice. Gap fillers can be provided or recommended from the factory. If the material will see outdoor exposure, Cuming Microwave can recommend applicable paints to maintain microwave performance.; C-RAM FLX can also be supplied with a pressure sensitive adhesive backing. While not as strong as liquid adhesives, it will provide an adequate bond in many applications, particularly when one is bonding smaller pieces. Simply peel off the backing, and press the part onto the cleaned substrate surface. If additional bond strength is required, apply the part to a primed surface, and apply heat with a heat gun for 1-2 minutes to effect a good bond.

Show in full

Plastics and Elastomers End Uses

Marine Applications