Ashlene® 520-13G Nylon 66, 13% Glass Reinforced
- Chemical Family
- Polyamides
Ashlene® 520-13G Nylon 66, 13% Glass Reinforced is a 13% Glass reinforced.
Product families
Applications
Applications
- Automotive & Transportation — Other Automotive & Transportation Applications; Consumer Goods — Other Consumer Goods Applications; Electrical & Electronics — Other Electrical & Electronics Applications
Industrial — Leather & Textiles
- Textile Manufacturing
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Ashlene
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 4300.0 - 4300.0 MPa
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hardness, Rockwell | 119 | Scale R | ASTM D785 |
| Izod Impact, Notched | 0.59 | J/cm | ASTM D256 |
| Tensile Strength, Yield | 90 | Mpa | ASTM D638 |
| Elongation at Break | 4 | % | — |
| Flexural Modulus | 4.3 | GPa | ASTM D790 |
Table 2 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.23 | g/cc | ASTM D792 |
| Water Absorption | 0.9 | % | ASTM D570 |
| Linear Mold Shrinkage | 0.007 | cm/cm | ASTM D955 |
Table 3 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Point | 252 | °C | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 | °C | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 239 | °C | ASTM D648 |