ZOLTEK™ PX30 FABRIC PW03
- Chemical Family
- Carbon Fiber
ZOLTEK PX30 Woven Carbon Fabrics tailorability results from controlling the yield on rovings and yarns, and allows for a variety of finished composite thicknesses. The spun yarns have many surface fibrils that protrude in various directions at various lengths from the surface. This fiber loft contributes to high cross-ply tensile and interlaminar shear strengths for 2-D composite materials. Contour conformation without wrinkling is another advantage of spun yarn fabrics. ZOLTEK PX30 materials undergo high temperature carbonization process, involving a long temperature soak time, resulting in a very thermally stable and chemically pure fabric with low oxidation rate.
Properties
- Physical Form
- Fabric
Product families
- Carbon Fiber
Other characteristics
- Brand
- ZOLTEK
- Features
Good Thermal Stability, Heat Resistance, Thermal Stability
- Reinforcement Form
- Plain Weave Fabric, Woven Fabric
- Plain Weave Fabric
- Woven Fabric
- Reinforcement Material
- Carbon Fibers
- Markets
- Automotive & Transportation
- Building & Construction
- Technology
- Composite Materials
- Certification
ZOLTEK PX30 Fabrics are manufactured in accordance with ZOLTEK's written and published data. A Certificate of Conformance is provided with each shipment.
- Packaging Type
- Rolls
- Composites End Use
- Brake Pads
- Clutch Linings
- Composite Materials
- Material Features
- Good Thermal Stability
- Heat Resistance
- Composite Materials Functions
- Reinforcement
Technical data
Table 1 of 1
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Areal Weight | 115 | g/m2 |
| Count (W x F) | 175 x 175 | Yarns / 10 cm |
| Thickness | 406 | microns |
| Standard Widths | 838 | mm |
| Roll Length | 73 | m |
| Yarn Input | 43888 | — |
| Electrical Resistivity | 0.0014 (0.00055) | ohm-cm (ohm-in) |
| Carbon Content | 99 | % |
| Density | 1.75 (0.063) | g/cc (lb/in3) |
| Oxidation Rate per hour at 932°F (500°C) | 1 | % |