To catalogue
Remo Polytechnik PC54 BK002
- Chemical Family
- Polycarbonate (PC)
Remo Polytechnik PC54 BK002 is a black unfilled polycarbonate.
Product families
Applications
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
- Other Automotive Applications
Electrical & Electronics — Devices & Assemblies
- Other Devices & Assemblies
Electrical & Electronics — Parts & Components
- Other Parts & Components
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Polymer Name
- Polycarbonate (PC)
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Certifications and Compliance
- EU Compliant
- ISO 14001
- UL 94
- Plastics and Elastomers End Uses
- Automotive Components
- Automotive Exterior Parts
- Automotive Interior Parts
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact, Notched (-30°C) | 20.0 | kJ/m | ISO 180/1A |
| Izod Impact, Notched (23°C) | 50.0 | kJ/m | ISO 180/1A |
| Izod Impact, un-notched (-30°C) | NB | kJ/m | ISO 180/1 |
| Izod Impact, un-notched (23°C) | NB | kJ/m | ISO 180/1U |
| Strain at Break (23°C) | min. 20 | % | ISO 527 |
| Tensile Modulus (23°C) | 2250.0 | MPa | ISO 527 |
| Yield Strength (23°C) | 65.0 | MPa | ISO 527 |
Table 2 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Abbreviation | PC | — | ISO 1043 |
| Density | 1.19 | g/cm3 | ISO 1183 |
| Melt Flow Rate (1.2kg, 300°C) | 12.0 | g/10 | ISO 1133 |
| Moisture Content | max. 0.1 | % | ISO 15512 |
| Molding Shrinkage (Parallel / Normal) | 0.5 | % | ISO 15512 |
| Moisture Absorption (50% RH, 23°C) | 0.2 | % | ISO 62 |
Table 3 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deformation Temperature (0.45 MPa ) | 125.0 | °C | ISO 75 |
| Heat Deformation Temperature (1.80 MPa) | 115.0 | °C | ISO 75 |
| Vicat Softening Temperature (50N) | 140.0 | °C | ISO 306 |
Table 4 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 225.0 | V | IEC 60112 |
| Surface Resistivity | 1.0e+15 | Ohm | IEC 60093 |
| Volume Resistivity | 1.0e+15 | Ohm. cm | IEC 60093 |
Table 5 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flame Rating (1.6mm) | HB | — | UL 94 |
| Glow Wire lgnitability Temperature (2 mm plaque) | 825.0 | °C | IEC 60695 |
| Flame Rating (0.75 mm) | HB | — | UL 94 |
Table 6 of 6
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure | Low | — |
| Drying | 120 / 3 - 4 | °C/hr |
| Feed Throat Temperature | 60 - 80 | °C |
| Hold Pressure | 60 - 120 | — |
| Injection Speed | Medium - Fast | — |
| Mold Temperature | 80 - 100 | MPa |
| Processing Temperature | 260 - 300 | °C |