SHD Composites MTC510FRB
- Chemical Family
- Epoxy & Epoxy Derivatives
Shanghai Sunwise Chemical MTC510FRB is a flame retardant epoxy resin system designed to cure between 80°C and 120°C allowing flexibility in component manufacture. It is a toughened, flame retarded epoxy resin system designed for component manufacturing that can be supplied on a variety of fabrics and in UD format to meet your cost and manufacturing requirements. This resin system color is black.
Product families
- Thermoset Prepregs
Other characteristics
- Functions
- Prepreg
- Polymer Name
- Epoxy Resins & Compounds
- Processing Methods
- Prepreg Processing
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Sports & Recreation
- Key Features
Cure temperature from 80°C to 120°C; Service temperature up to 125°C after post cure; Low CTE and shrinkage; Work life at 20°C: 30 days; Storage life at -18°C: 12 months; Very low VOC content – no added solvents during manufacture; Excellent surface finish; Flame retardant: Compliant with FAR 25.853 (60s vertical burn, smoke and toxic gas emissions) Rated UL94 V0 (4mm laminate), UL94 V1 (2mm laminate)
- Technology
- Composite Materials
- Packaging Type
- Bags
- Labeling Claims
- Low VOC
- Health and Safety
This material contains epoxy resin which can cause allergic reactions with skin contact and must avoid repeated and prolonged skin contact.; The following precautions must be taken when using epoxy resin prepregs:; Overalls must be worn; Impervious gloves must be worn.; Curing schedule is meant to be as a guide only and is subject to local conditions.; To avoid exotherm, particular care must be taken with thick laminates.; Ramp rates must not exceed 3.0°C/min during initial cure and 0.3°C/min during post cure.
- Material Features
- Flame Retardant
- Good Surface Appearance
- Improved Flexibility
- Low Shrinkage
- Storage and Out Life
This material should be kept frozen at -18°C. It must be kept sealed in a polythene bag which must not be opened until fully thawed to room temperature. If the material is not fully used, then the material must be resealed in the polythene bag to prevent moisture absorption.
- Typical Applications
- Flame retardant – General purpose
- Recommended Cure Cycle
Curing Schedule is meant to be a guide only and is subject to local conditions.; To avoid exotherm particular care must be taken with thick laminates.; Ramp rates must not exceed 3.0°C per minute during initial cure.; Ramp rates must not exceed 0.3°C per minute during post cure (free standing).
- Composite Materials Functions
- Prepreg
- Composites Processing Methods
- Prepreg Processing
Technical data
Table 1 of 1
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Cure Temperature | 80 - 120 | °C | — |
| Cure Time | 16 - 1 | — | hrs,mins |
| Outlife | 30 | — | months |
| Tg Onset | 130 | — | — |
| Tg Peak | 148 | — | — |
| Service Temperature | 125 | °C | — |