ENYDYNE® H 86291 TF
ENYDYNE® H 86291 TF - Unsaturated polyester resin in styrene,DCPD. It is used to produce isothermal sandwich panels through hand lay up and spray up,injection molding,rtm method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Automotive & Transportation — Transportation
- Rail & Mass Transit
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- ENYDYNE
- End Uses
- Pipes, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
Hand Lay-up, Resin Transfer Molding (RTM), Spray Lay-up
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Shelf LIfe
- 4 Months (23°C in Dark )
- Technology
- Composite Materials
- Product Safety
Stir the resin before use, without use air bubbles, The final Fire resistance properties could change following the final structure of the piece and its use's condition. It will be necessary to verify the final properties on a prototype before industrial production.
- Application Methods
- Spray
- Composites End Use
- Pipes
- Tanks
- Material Features
- Flame Retardant
- HIGHLIGHTS
- Fire retardand properties
- Filled
- Very good glass wet-out
- Medium viscosity
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Hand Lay-up
- Resin Transfer Molding (RTM)
- Spray Lay-up
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Brookfield Viscosity at 23°C, sp 3 rpm 50 | 700 - 900 | mPa.s | MT-CUT23V |
| Solid Content | 72 - 76 | % | MT-CU001C |
| Gel Time at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 12-16 | minutes | MT-CU152R |
| Peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 33 - 43 | — | MT-CU152R |
| Exothermic peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 45 - 55 | °C | MT-CU152R |
| Specific weight at 20°C | 1,6 | g/cm3 | — |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile strength at 40°C for 16h/+ 2 h at 90°C | 45 | MPa | ISO 527 (2012) |
| Tensile Modulus at 40°C for 16h/+ 2 h at 90°C | 3550 | MPa | ISO 527 (2012) |
| Flexural strength at 40°C for 16h/+ 2 h at 90°C | 90 | MPa | ISO 178 (2011) |
| Flexural modulus at 40°C for 16h/+ 2 h at 90°C | 3500 | MPa | ISO 178 (2011) |
| HDT at 40°C for 16h/+ 2 h at 120°C | 65 | °C | ISO 75 -2A (2013) |
| Elongation at break at 40°C for 16h/+ 2 h at 90°C | 1,55 | % | ISO 527 (2012) |