POLYCOR® M1 PA WHITE
POLYCOR® M1 PA WHITE - A pre-accelerated gel coat base on unsaturated polyester resin. It is cured using MEKP peroxide.Product is recommended for the manufacture of industrial pieces requiring additional fire retardence. The product was designed for INTERNAL pieces ONLY.
Product families
Applications
Automotive & Transportation — Transportation
- Aerospace & Aviation
- Rail & Mass Transit
Product Families
Composite Materials — Surface Finishes
- Gelcoats & Topcoats
Other characteristics
- Brand
- POLYCOR
- Color
- Custom, Off White, White
- Custom
- Off White
- White
- Features
- Flame Retardant
- Functions
- Surface Finish
- Markets
- Automotive & Transportation
- Technology
- Composite Materials
- Application Methods
- Spray
- Material Features
- Flame Retardant
- Shelf Life Storage
4 Months .. When the product is sealed in its original packing, stored indoors away from direct sunlight and direct heat sources and ideally at ambient temperature between 15°C and 25°C .
- Composite Materials Functions
- Surface Finish
Technical data
Table 1 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at break | 2,2 | % | ISO 527 |
| H.D.T (NFT ISO 75)......... | 57 | °C | — |
| Tensile strength | 55 | MPa | — |
Table 2 of 3
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Density | 1,52 - 1,58 | — |
| Sag Resistance | 500 | μm - wet |
| Hide depends colour | 500 - 700 | μm - wet |
| Color | Depends colour | — |
| Viscosity (25°C - Spindle 5-5 rpm) | 300 - 350 | dPa.s |
| Solid Content (15mn at 150°C) | 70 - 76 | % |
| Thixotropic Index (5/50 rpm) | 6,5 - 8,0 | — |
Table 3 of 3
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Film cure (500μ - 20°C - 2% MEKP) | 40 - 50 | mn |
| Gel Time (200g - 25°C - 1,8% MEKP) | 10-14 | mn |
| Peak Time (200g - 25°C - 1,8% MEKP) | 30 - 40 | mn |
| Peak exotherm (°C) (200g - 25°C - 1,8% MEKP) | 100 - 140 | — |