DISTITRON® 279
DISTITRON® 279 - Unsaturated polyester resin in styrene,Ortophthalic-Neopentylic. It is used to produce bmc and smc manufacture,very good mechanical properties through hot press molding method.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
- Chassis & Brake
- Exterior & Body
- Interior
- Powertrain & UTH
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Electrical & Electronics — Parts & Components
- Housings & Enclosures
- Printed Circuit Boards (PCBs)
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Automotive & Transportation — Transportation
- Aerospace & Aviation
- Marine
- Rail & Mass Transit
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- End Uses
- Pipes, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
- Compression Molding
- Color
- Yellow
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Composites End Use
- Pipes
- Tanks
- Material Features
- Good Mechanical Properties
- HIGHLIGHTS
- High reactivity
- To manufacture Class A SMC/BMC
- Clear unaccelerated
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Compression Molding
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Brookfield Viscosity at 25°C, sp 3 rpm 20 | 1800 - 2000 | mPa.s | MT-CU025V |
| Solid Content | 63 - 66 | % | MT-CU001C |
| Curing Time at 130°C + 1% TBPEH | 95 - 115 | sec | RS.03.G |
| Exothermic peak at 130°C + 1% TBPEH | 200 - 240 | °C | RS.03.G |
| Specific weight at 20°C | 1,11 | g/cm3 | — |
| Acidity at 130°C + 1% TBPEH | 14,5 - 19,5 | mg KOH/g | MT-CU001I |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile strength at 70°C for 16h/ +2h at 100°C + 1h at 100°C | 45 | MPa | ISO 527 (2012) |
| Tensile Modulus at 70°C for 16h/ +2h at 100°C + 1h at 100°C | 3700 | MPa | ISO 527 (2012) |
| Flexural strength at 70°C for 16h/ +2h at 100°C + 1h at 100°C | 90 | MPa | ISO 178/B (2010) |
| Flexural modulus at 70°C for 16h/ +2h at 100°C + 1h at 100°C | 3600 | MPa | ISO 178/B (2010) |
| HDT at 70°C for 16h/ +2h at 100°C + 1h at 100°C | 124 | °C | ISO 75 -2A (2013) |
| Barcol Hardness at 25°C at 70°C for 16h/ +2h at 100°C + 1h at 100°C | 50 | — | ASTM D 2583 (2007) |
| Elongation at break at 70°C for 16h/ +2h at 100°C + 1h at 100°C | 1,4 | % | ISO 527 (2012) |