DISTITRON® 135 SX
DISTITRON® 135 SX - Unsaturated polyester resin in styrene,Isophthalic. It is used to produce marine,boats through hand lay up and spray up method.
Product families
Applications
Automotive & Transportation — Transportation
- Marine
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- Polymer Name
- Polyester (unspecified)
- Processing Methods
- Hand Lay-up, Spray Lay-up
- Color
- Blue
- Markets
- Automotive & Transportation
- Shelf LIfe
- 3 Months (23°C in Dark )
- Technology
- Composite Materials
- Product Safety
Stir the resin before use, without use air bubbles, As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.
- Application Methods
- Spray
- HIGHLIGHTS
- Low styrene emission
- Low styrene content
- With catalyst indicator
- Preaccelerated
- Thixotropic
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Hand Lay-up
- Spray Lay-up
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific weight at 20°C | 1, 11 | g/cm3 | — |
| Exothermic peak at 20°C + 1,5% MEKP50 | 165 - 195 | °C | RS.08.G |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 750 - 960 | mPa.s | MT-CUT25V |
| Solid Content | min. 65 | % | MT-CU001C |
| Gel Time at 20°C + 1,5% MEKP50 | 28 - 36 | minutes | RS.08.G |
| Delta at 20°C + 1,5% MEKP50 | 10-17 | minutes | RS.08.G |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3400 | MPa | ISO 178/B (2010) |
| Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 55 | MPa | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3500 | MPa | ISO 527 (2012) |
| Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 105 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 67 | °C | ISO 75 -2A (2013) |
| Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 37 | — | ASTM D 2583 (2007) |
| Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 2, 0 | % | ISO 527 (2012) |