Polynt Group SMC LS 3000 R18
Polynt Group SMC LS 3000 R18 is a sheet molding compound based on an unsaturated polyester resin, halogen-free, reinforced with glass fibers. This SMC has been developed for general purpose. SMC LS 3000 R18 joint good mechanical properties and good fluidity. SMC LS 3000 R18 is formulated according to RoHS, REAC regulation SVHC and WEEE European legislation.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Electrical & Electronics — Parts & Components
- Housings & Enclosures
- Printed Circuit Boards (PCBs)
Automotive & Transportation — Transportation
- Rail & Mass Transit
Product Families
Composite Materials — Prepregs & Molding Compounds
- Sheet Molding Compounds (SMC)
Other characteristics
- Functions
- Molding Compound
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Technology
- Composite Materials
- Handling
Storage at 15-25°C, in dry ambient and out of direct sun light; Molding time 40 s/mm; Molding pressure 70 - 110 bar; Molding temperature 140 – 160°C
- Composite Materials Functions
- Molding Compound
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Rockwell Hardness | 80 | HRm | ISO 2039-2 |
| Heat distortion temperature HDT | min. 200 | °C | ISO 75 |
| Quantity of glass | 18 | % | — |
| Flexural modulus | 9 | MPa | ISO 14125A |
| Linear Shrinkage | 0,15 | % | ISO 2577 |
| Density | 1,8 | g/cm3 | ISO 1183 |
| Surface resistivity | 10^14 | Ω | IEC 93 |
| Water absorption | max. 0,2 | % | ISO 62 Met. 1 |
| Impact strength (Charpy) | 50 | KJ/m2 | ISO 179 |
| Flexural strength | 110 | MPa | ISO 14125A |
| flammability | HB | Class | UL 94 |