Polynt Group SMC LP 6700 LW
Polynt Group SMC LP 6700 LW is a sheet molding compound based on an unsaturated polyester resin reinforced with glass fibers. SMC LP 6700 LW is a low weight compounds and it has been developed for structural parts. SMC LP 6700 LW meets mechanical and thermal properties with reduction weight of the final parts. SMC LP 6700lw is formulated according to RoHS, REAC regulation SVHC and WEEE European legislation.
Product families
Applications
Automotive & Transportation — Automotive
- Chassis & Brake
- Exterior & Body
- Interior
- Powertrain & UTH
Automotive & Transportation — Transportation
- Aerospace & Aviation
- Marine
- Rail & Mass Transit
Product Families
Composite Materials — Prepregs & Molding Compounds
- Sheet Molding Compounds (SMC)
Other characteristics
- Functions
- Molding Compound
- Markets
- Automotive & Transportation
- Technology
- Composite Materials
- Material Features
- Good Mechanical Properties
- Handling
Storage in a dry place at 15-25°C, out of direct sunlight; Molding time 40 s/mm; Molding pressure 70 - 110 bar; Molding temperature 140 – 160°C
- Composite Materials Functions
- Molding Compound
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat distortion temperature HDT | min. 200 | °C | ISO 75 |
| Linear Shrinkage | 0,02 | % | ISO 2577 |
| Flexural strength | 80 | MPa | ISO 14125A |
| Density | 1,35 | g/cm3 | ISO 1183 |
| Quantity of glass | 25 | % | ISO 11667 |
| Water absorption | max. 0,2 | % | ISO 62 Met. 1 |
| Impact strength (Charpy) | 50 | KJ/m2 | ISO 179 |
| Glass fibre length | 25 | mm | — |
| Flexural modulus | 6 | MPa | ISO 14125A |
| Surface resistivity | 10^13 | Ω | IEC 93 |
| Speed of the flame | max. 80 | mm/min | SAE J369 |