POLYCOR® LP PA WHITE 9199
- Chemical Family
- Isophthalics
POLYCOR® LP PA WHITE 9199 - A pre-accelerated gel coat based on modified Isophthalic unsaturated polyester resin. It is cured using MEKP peroxide.This product is formulated for use in a variety of industrials composite parts.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Automotive & Transportation — Transportation
- Rail & Mass Transit
Product Families
Composite Materials — Surface Finishes
- Gelcoats & Topcoats
Other characteristics
- Brand
- POLYCOR
- Color
- Custom, Off White, White
- Custom
- Off White
- White
- Functions
- Surface Finish
- Markets
- Automotive & Transportation
- Building & Construction
- Technology
- Composite Materials
- Application Methods
- Spray
- Shelf Life Storage
4 Months .. When the product is sealed in its original packing, stored indoors away from direct sunlight and direct heat sources and ideally at ambient temperature between 15°C and 25°C .
- Composite Materials Functions
- Surface Finish
Technical data
Table 1 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at break | 3,8 | % | ISO 527 |
| H.D.T (NFT ISO 75)......... | 54 | °C | — |
| Tensile strength | 59 | MPa | — |
Table 2 of 3
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Density | 1,05 - 1,28 | — |
| Sag Resistance | 500 | μm - wet |
| Hide depends colour | 500 - 700 | μm - wet |
| Color | Depends colour | — |
| Viscosity (25°C - Spindle 4-4 rpm) | 110 - 150 | dPa.s |
| Solid Content (15mn at 150°C) | 69 - 73 | % |
| Thixotropic Index (2/20 rpm) | 6,0 - 7,5 | — |
Table 3 of 3
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Film cure (500μ - 20°C - 2% MEKP) | 45 - 60 | mn |
| Gel Time (200g - 25°C - 1,8% MEKP) | 12-15 | mn |
| Peak Time (200g - 25°C - 1,8% MEKP) | 15 - 35 | mn |
| Peak exotherm (°C) (200g - 25°C - 1,8% MEKP) | 150 - 210 | — |