Polynt Group HUP 31838/30 RN-1090
Polynt Group HUP 31838/30 RN-1090 is generally used in aeronautical applications.
Product families
Applications
Automotive & Transportation — Transportation
- Aerospace & Aviation
Product Families
Composite Materials — Prepregs & Molding Compounds
- Sheet Molding Compounds (SMC)
Other characteristics
- Functions
- Molding Compound
- Markets
- Automotive & Transportation
- Technology
- Composite Materials
- Handling
- Storage condition store dry at max
- 25 °C and out of direct sun light
- Molding time > 25 sec
- /mm
- Molding pressure 80 - 120 bar
- Molding temperature 140 - 150 °C
- Composite Materials Functions
- Molding Compound
Technical data
Table 1 of 1
17 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance | 10^13 | Ohm | IEC 93 |
| Shrinkage | 0,03 | % | ISO 2577 |
| fire test aviation | 1,2 | mm | CS/JAR/FAR 25.853 App. F, Part I,a-1. Ii |
| impact strength | 65 | KJ/m2 | ISO 179 |
| Specific Density | 1,62 | g/cm3 | ISO 1183 A |
| Flexural modulus | 8 | N/mm2 | ISO 14125 |
| fibre length | 25 | mm | DF PA3.01 |
| surface weight | 3 | g/m2 | ISO 10352 |
| Specific volume resistance | 1014 | Ohm x cm | IEC 93 |
| Water absorption | max. 50 | mg | ISO 62 |
| Flexural strength | 150 | N/mm2 | ISO 14125 |
| fibre Content | 30 | % | ISO 1172 |