Polynt Group SMC S 8010
Polynt Group SMC S 8010 is a sheet molding compound based on an blend of different thermoset polymers reinforced with glass fibers. SMC S 8010 has been developed for structural parts. SMC S 8010 joints excellent mechanical and thermal properties. SMC S 8010 is formulated according to RoHS, REAC regulation SVHC and WEEE European legislation.
Product families
Applications
Automotive & Transportation — Automotive
- Chassis & Brake
- Exterior & Body
- Interior
- Powertrain & UTH
Automotive & Transportation — Transportation
- Aerospace & Aviation
- Marine
- Rail & Mass Transit
Product Families
Composite Materials — Prepregs & Molding Compounds
- Sheet Molding Compounds (SMC)
Other characteristics
- Functions
- Molding Compound
- Markets
- Automotive & Transportation
- Technology
- Composite Materials
- Material Features
- Flame Retardant
- Good Mechanical Properties
- Handling
Storage in a dry place at 15-25°C, out of direct sunlight; Molding time 40 s/mm; Molding pressure 70 - 110 bar; Molding temperature 140 – 160°C
- Composite Materials Functions
- Molding Compound
Technical data
Table 1 of 1
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Rockwell Hardness | 80 | Scale M | ISO 2039-2 |
| Linear Shrinkage | 0,0 | % | ISO 2577 |
| Poisson’s ratio | 0,29 | — | ASTM D 638 |
| Density | 1,65 | g/cm3 | ISO 1183 |
| Water absorption | max. 0,2 | % | ISO 62 Met. 1 |
| Heat distortion temperature HDT | min. 240 | °C | ISO 75 |
| Flexural strength | 420 | MPa | ISO 14125A |
| Flexural modulus | 18 | MPa | ISO 14125A |
| Impact strength (Charpy) | 240 | KJ/m2 | ISO 179 |