Polynt Group SMC LS 3200 R20 C20
Polynt Group SMC LS 3200 R20 C20 is a sheet molding compound based on an unsaturated polyester resin reinforced with glass fibers. This SMC has been developed for structural parts. SMC LS 3200 R20 C20 meets mechanical and thermal properties with reduction weight of the final parts. SMC LS 3200 R20 C20 is formulated according to RoHS, REAC regulation SVHC and WEEE European legislation.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Product Families
Composite Materials — Prepregs & Molding Compounds
- Sheet Molding Compounds (SMC)
Other characteristics
- End Uses
- Pipes, Tanks
- Functions
- Molding Compound
- Markets
- Industrial
- Technology
- Composite Materials
- Composites End Use
- Pipes
- Tanks
- Material Features
- Good Mechanical Properties
- Handling
Storage in a dry place at 15-25°C, out of direct sunlight; Molding time 40 s/mm; Molding pressure 70 - 110 bar; Molding temperature 140 – 160°C
- Composite Materials Functions
- Molding Compound
Technical data
Table 1 of 1
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Linear Shrinkage Trasversal | 0,00 | % | ISO 2577 |
| Linear Shrinkage Longitudinal | 0,20 | % | ISO 2577 |
| Density | 1,6 | g/cm3 | ISO 1183 |
| Water absorption | max. 0,2 | % | ISO 62 Met. 1 |
| Quantity of continuous glass | 20 | % | — |
| Quantity of random glass | 20 | % | — |
| Flexural strength Trasversal | 400 | MPa | ISO 14125A |
| Flexural strength Longitudinal | 100 | MPa | ISO 14125A |
| Flexural modulus Trasversal | 19 | MPa | ISO 14125A |
| Flexural modulus Longitudinal | 6 | MPa | ISO 14125A |
| Impact strength (Charpy) Trasversal | 180 | KJ/m2 | ISO 179 |
| Impact strength (Charpy) Longitudinal | 60 | KJ/m2 | ISO 179 |