NORSODYNE® C 13133 L
NORSODYNE® C 13133 L - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce agglomerated and engineered stones through casting method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- NORSODYNE
- End Uses
- Structural Components
- Polymer Name
- Polyester (unspecified)
- Markets
- Building & Construction
- Shelf LIfe
- 9 Months (23°C in Dark )
- Technology
- Composite Materials
- Composites End Use
- Structural Components
- Material Features
- Good UV Protection
- HIGHLIGHTS
- Low reactivity
- Low viscosity
- Light stabilized
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
Technical data
Table 1 of 2
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 62 - 66 | % | MT-CU001C |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 410 - 470 | mPa.s | MT-CU023V |
| Gel Time at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 10-13 | minutes | MT-CU152R |
| Peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 27 - 33 | minutes | MT-CU152R |
| Exothermic peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 110 - 130 | °C | MT-CU152R |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at break at 40°C for 16h | 1,9 | % | ISO 527 (2012) |
| Tensile strength at 40°C for 16h | 49 | MPa | ISO 527 (2012) |
| Tensile Modulus at 40°C for 16h | 3705 | MPa | ISO 527 (2012) |
| Flexural strength at 40°C for 16h | 105 | MPa | ISO 178 (2011) |
| Flexural modulus at 40°C for 16h | 3370 | MPa | ISO 178 (2011) |
| HDT at 40°C for 16h / +2h at 120°C | 59 | °C | ISO 75 -2A (2013) |