NORSODYNE® C 16237
NORSODYNE® C 16237 - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce abrasives,chips through casting method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- NORSODYNE
- End Uses
- Structural Components
- Polymer Name
- Polyester (unspecified)
- Markets
- Building & Construction
- Shelf LIfe
- 9 Months (23°C in Dark )
- Technology
- Composite Materials
- Composites End Use
- Structural Components
- HIGHLIGHTS
- High reactivity
- High viscosity
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
Technical data
Table 1 of 2
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 65 - 69 | % | MT-CU001C |
| Exothermic peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 150 - 170 | °C | MT-CU152R |
| Brookfield Viscosity at 23°C, sp 3 rpm 50 | 950 - 1150 | mPa.s | MT-CU023V |
| Gel Time at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 13:30 - 19:30 | minutes | MT-CU152R |
| Peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 25 - 32 | — | MT-CU152R |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at break at 40°C for 16h / + 2 h at 90°C | 1,25 | % | ISO 527 (2012) |
| Flexural strength at 40°C for 16h / + 2 h at 90°C | 115 | MPa | ISO 178 (2011) |
| Tensile strength at 40°C for 16h / + 2 h at 90°C | 40 | MPa | ISO 527 (2012) |
| Tensile Modulus at 40°C for 16h / + 2 h at 90°C | 3475 | MPa | ISO 527 (2012) |
| Flexural modulus at 40°C for 16h / + 2 h at 90°C | 3770 | MPa | ISO 178 (2011) |
| HDT at 40°C for 16h / + 2 h at 120°C | 106 | °C | ISO 75 -2A (2013) |