ENYDYNE® H 88222 TA
ENYDYNE® H 88222 TA - Unsaturated polyester resin in styrene,DCPD. It is used to produce parts with high resistance to fire through hand lay up and spray up,injection molding,rtm method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Automotive & Transportation — Transportation
- Rail & Mass Transit
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- ENYDYNE
- End Uses
- Pipes, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
Hand Lay-up, Resin Transfer Molding (RTM), Spray Lay-up
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Product Safety
Stir the resin before use, without use air bubbles
- Application Methods
- Spray
- Composites End Use
- Pipes
- Tanks
- HIGHLIGHTS
- Preaccelerated
- Thixotropic
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Hand Lay-up
- Resin Transfer Molding (RTM)
- Spray Lay-up
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 56 - 60 | % | MT-CU001C |
| Specific weight at 20°C | 1,11 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 440 - 600 | mPa.s | MT-CUT23V |
| Gel Time | 20 - 25 | minutes | MT-CU151R |
| Exothermic peak | 135 - 155 | °C | MT-CU151R |
| Reactivity at 23°C | + 1,5 | % | MEKP50 |
| Peak (23°C) | 28 - 33 | — | — |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Curing Cycle at 40°C + 2 h at 90°C (at 120°C for HDT)) | 16 (2) | hr | — |
| Tensile strength | — | MPa | ISO 527 (2012) |
| Tensile Modulus | 3200 | MPa | ISO 527 (2012) |
| Elongation at break | 2 | % | ISO 527 (2012) |
| Flexural strength | 65 | MPa | ISO 178 (2011) |
| Flexural modulus | 2700 | MPa | ISO 178 (2011) |
| HDT | 55 | °C | ISO 75 -2A (2013) |