Polynt Group SMC LS 3600 R25 AE

Name: Polynt Group SMC LS 3600 R25 AE
Brand: Polynt Group

Polynt Group SMC LS 3600 R25 AE is a sheet molding compound based on an unsaturated polyester resin, fire retardant grade, reinforced with glass fibers. This SMC has been developed for electrical application. SMC LS 3600 R25 AE joint good mechanical properties and excellent fire protection grade. SMC LS 3600 R25 AE is certified V0 1, 5 mm by UL laboratories. SMC LS 3600 R25 AE is formulated according to RoHS, REAC regulation SVHC and WEEE European legislation.

Product families

Applications

Consumer Goods — Appliances & Electronics

Electrical & Electronics — Parts & Components

Housings & Enclosures
Printed Circuit Boards (PCBs)

Automotive & Transportation — Transportation

Rail & Mass Transit

Product Families

Composite Materials — Prepregs & Molding Compounds

Sheet Molding Compounds (SMC)

Other characteristics

Functions: Molding Compound
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Technology: Composite Materials
Material Features: Flame Retardant
Good Mechanical Properties
Handling: Storage at 15-25°C, in dry ambient and out of direct sun light; Molding time 40 s/mm; Molding pressure 70 - 110 bar; Molding temperature 140 – 160°C
Composite Materials Functions: Molding Compound

Technical data

Table 1 of 2

14 rows

Characteristic	Value	Unit	Method
Rockwell Hardness	80	HRm	ISO 2039-2
Glow wire GWFI	960	°C	IEC 695-2-1
Heat distortion temperature HDT	min. 200	°C	ISO 75
Flexural modulus	9.5	MPa	ISO 14125A
arc resistance	min. 180	s	ASTM D 495
Linear Shrinkage	0,1	%	ISO 2577
Density	1,75	g/cm3	ISO 1183
Quantity of glass	25	%	ISO 11667
Impact strength (Charpy)	70	KJ/m2	ISO 179
Surface resistivity	10^14	Ω	IEC 93
Volume resistivity	10^14	Ω mm	IEC 93
Water absorption	max. 0,2	%	ISO 62 Met. 1

Table 2 of 2

1 row

Characteristic	Value
Flammability	V0 (1,5)