NORSODYNE® H 32433 TA
NORSODYNE® H 32433 TA - Unsaturated polyester resin in styrene,Isophthalic. It is used to produce marine,boats through hand lay up and spray up method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Automotive & Transportation — Transportation
- Marine
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- NORSODYNE
- End Uses
- Pipes, Structural Components, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
- Hand Lay-up, Spray Lay-up
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Product Safety
Stir the resin before use, without use air bubbles
- Application Methods
- Spray
- Composites End Use
- Pipes
- Structural Components
- Tanks
- HIGHLIGHTS
- Low reactivity
- Low exothermic peak
- Preaccelerated
- Thixotropic
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Hand Lay-up
- Spray Lay-up
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific weight at 20°C | 1,12 | g/cm3 | — |
| Solid Content | 55 - 59 | % | MT-CU001C |
| Brookfield Viscosity at 23°C, sp 3 rpm 50 | 700 - 900 | mPa.s | MT-CUT23V |
| Gel Time at 23°C + 1,5% MEKP50 | 34 - 40 | minutes | MT-CU151R |
| Peak at 23°C + 1,5% MEKP50 | 65 - 75 | minutes | MT-CU151R |
| Exothermic peak at 23°C + 1,5% MEKP50 | 60 - 80 | °C | MT-CU151R |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at break at 40°C for 16h | 2,75 | % | ISO 527 (2012) |
| Tensile strength at 40°C for 16h | 75 | MPa | ISO 527 (2012) |
| Tensile Modulus at 40°C for 16h | 3884 | MPa | ISO 527 (2012) |
| Flexural strength at 40°C for 16h | 107 | MPa | ISO 178 (2011) |
| Flexural modulus at 40°C for 16h | 3503 | MPa | ISO 178 (2011) |
| HDT at 40°C for 16h /+2h for 120°C | 68 | °C | ISO 75 -2A (2013) |