Polynt Group SMC LPMC 7200 Low pressure
Polynt Group SMC LPMC 7200 Low pressure is a sheet molding compound based on an unsaturated polyester resin reinforced with glass fibers. SMC LPMC 7200 is studied to be molded at low pressure and has been developed for co-molding with phenolic foam. SMC LPMC 7200 is formulated according to RoHS, REAC regulation SVHC and WEEE European legislation.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Product Families
Composite Materials — Prepregs & Molding Compounds
- Sheet Molding Compounds (SMC)
Other characteristics
- Functions
- Molding Compound
- Markets
- Building & Construction
- Technology
- Composite Materials
- Handling
Storage at 15-25°C, in dry ambient and out of direct sun light; Molding time 40 s/mm; Molding pressure 20 - 100 bar; Molding temperature 140 – 160°C
- Composite Materials Functions
- Molding Compound
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Rockwell Hardness | 80 | Scale M | ISO 2039-2 |
| Impact strength (Charpy) | 35 | KJ/m2 | ISO 179 |
| Heat distortion temperature HDT | min. 200 | °C | ISO 75 |
| Flexural strength | 90 | MPa | ISO 14125A |
| Linear Shrinkage | 0,1 | % | ISO 2577 |
| Density | 1,6 | g/cm3 | ISO 1183 |
| Mass per unit area | 3,0 | Kg/m2 | ISO 10352 |
| Length of glass | 25 | mm | — |
| Quantity of glass | 13 | % | ISO 11667 |
| Flexural modulus | 9000 | MPa | ISO 14125A |
| Water absorption | max. 0,5 | % | ISO 62 Met. 1 |