DISTITRON® VE 102 V9
DISTITRON® VE 102 V9 - Bisphenol-A Epoxy Resin based vinyl ester in styrene. It is used to produce production of gelcoat,profiles through mix with fillers and/or additives,pultrusion.
Identification
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Automotive & Transportation — Transportation
- Marine
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- End Uses
- Pipes, Tanks
- Polymer Name
- Vinyl Ester Resin
- Processing Methods
- Pultrusion
- Color
- Yellow
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Composites End Use
- Pipes
- Tanks
- HIGHLIGHTS
- Certificate RINA
- High thermal resistance
- Clear unaccelerated
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Pultrusion
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 57 - 61 | % | MT-CU001C |
| Specific weight at 20°C | 1,07 | g/cm3 | — |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 820 - 980 | mPa.s | MT-CU025V |
| Gel Time at 25°C + 1% Co 1% + 2% MEKP50 | 21 - 30 | minutes | RS.08.G |
| Delta at 25°C + 1% Co 1% + 2% MEKP50 | 10-16 | minutes | RS.08.G |
| Exothermic peak at 25°C + 1% Co 1% + 2% MEKP50 | 160 - 190 | °C | RS.08.G |
| Acidity at 25°C + 1% Co 1% + 2% MEKP50 | 17 - 24 | mg KOH/g | MT-CU001I |
Table 2 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3200 | MPa | ISO 527 (2012) |
| Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3100 | MPa | ISO 178/B (2010) |
| Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 40 | — | ASTM D 2583 (2007) |
| HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 105 | °C | ISO 75 -2A (2013) |
| Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 145 | MPa | ISO 178/B (2010) |
| Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 85 | MPa | ISO 527 (2012) |
| Glass transition at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 108 | °C | ASTM E 1545 (2011) |
| Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 6,5 | % | ISO 527 (2012) |